Performance of White Fused Alumina in Investment Casting
  
<ol>
 	<li>Investment Casting Shell Material</li>
</ol>
<a href="https://www.xinliabrasive.com/products/White-Fused-Alumina">White fused alumina</a> is produced by fusing high-quality industrial alumina at temperatures above 2000 °C. It offers exceptional purity (α-Al₂O₃ content &gt; 99–99.6%) and a high refractoriness of 2050 °C–2100 °C, with a low thermal expansion coefficient (approx. 8×10⁻⁶/°C). These properties make it an excellent alternative to traditional zircon sand as a prime shell material for investment casting. Its high particle uniformity (grain size distribution &gt; 95%) and good dispersion help create denser, more robust molds, significantly improving casting surface finish and dimensional accuracy while reducing defect rates.
 
<ol start="2">
 	<li>Mould Reinforcement</li>
</ol>
 With a Mohs hardness of 9.0 and excellent high-temperature strength retention (maintaining integrity above 1900 °C), <a href="https://www.xinliabrasive.com/products/White-Fused-Alumina">white fused alumina</a> extends mold service life by 30–50%. When used in molds or cores for cast iron, cast steel, or non-ferrous alloys, it effectively resists metal flow erosion and reduces the frequency of repairs and maintenance.

Advantages of White Fused Alumina
 <a href="https://www.xinliabrasive.com/products/White-Fused-Alumina" rel="attachment wp-att-5561"><img decoding="async" src="/wp-content/uploads/2025/07/white-fused-alumina-1024x576.jpg" class="aligncenter" alt="white fused alumina" /></a>
 (1) <a href="https://www.xinliabrasive.com/products/White-Fused-Alumina">High-Temperature Stability</a>
 White fused alumina offers outstanding thermochemical stability during casting operations. Its thermal expansion coefficient is about one-third that of conventional materials, helping to prevent mold cracking or casting deformation due to sudden temperature changes. Its low gas evolution (gas release &lt; 3 ml/g) minimizes porosity and blowhole defects.

(2) <a href="https://www.xinliabrasive.com/products/White-Fused-Alumina">Surface Finishing Quality</a>
 When used as a fine polishing powder (grain size 0.5–45 μm), white fused alumina delivers consistent, even abrasion that can achieve a casting surface roughness of Ra &lt; 0.8 μm. Its self-sharpening nature (breakage rate &lt; 5%) ensures sustained cutting efficiency and stable polishing results.

(3) <a href="https://www.xinliabrasive.com/products/White-Fused-Alumina">Process Adaptability</a>
 We offer adjustable grain sizes ranging from F12 to F10000 to suit diverse casting processes:
 
 Coarse grades (F12–F100): For mold release in complex structures, increasing demolding success rates by over 25%.

&nbsp;

Fine grades (F220–F1000): For producing high-precision ceramic cores with forming tolerances as tight as ±0.1 mm.
 
<ol start="3">
 	<li>Process Optimization Value</li>
</ol>
 (1) Cost Efficiency
 Replacing zircon sand with white fused alumina can reduce material costs by 30–40%. It also enables shell thickness to be reduced by 15–20% (typical shell thickness: 0.8–1.2 mm), shortening the shell-building cycle.

(2) Environmental Benefits
 With ultra-low heavy metal content (&lt; 0.01%), <a href="https://www.xinliabrasive.com/products/White-Fused-Alumina">white fused alumina </a>meets ISO 14001 environmental standards. Waste sand is 100% recyclable and can be reused in refractory production.
 
 Proven Applications
 
This material has been widely adopted in high-end fields such as aerospace turbine blades and medical device precision castings. Typical cases show that it can increase product pass rates from 85% to 97%.